Ultrasonic fatigue testing of AISI 304 and 316 stainless steels under environmental and immersion conditions
DOI:
https://doi.org/10.3221/IGF-ESIS.68.11Keywords:
Gigacycle fatigue, Stainless steels, fracture mechanisms, Fracture surfacesAbstract
Ultrasonic fatigue tests were carried out on stainless steel AISI 316 and 304, under two modalities: at room temperature and in immersion (water for 316 and antifreeze for 304 steels); all tests were carried out with a loading ratio R=-1. The results obtained in the tests at room temperature (without immersion), for both materials exhibited a significant increase in temperature, leaving heat marks on the narrow section of the specimens. This phenomenon occurred due to the low coefficient of thermal conductivity of these stainless steels (16.2 W/ (m °K)), and the recorded temperatures were around 200 °C, generating instantaneous failure of material. Analyzes of fracture surfaces on specimens tested at room temperature reveal that crack initiation was related to the high temperature, causing alteration at the granular scale of the material, followed by a typical behavior crack propagation and failure. For specimens tested under immersion conditions, it was possible to reduce the temperature below 100 °C, which solved the problem of failure due to thermal effect. The results for 316 stainless steel immersed in water showed a fatigue life of 1.188×1010 cycles at188 MPa of stress loading in the specimen; while specimens subjected to 263 MPa stress showed a fatigue life of around 7×106 cycles, representing a significant reduction with an approximate factor of 1700. On the other hand, specimens of 304 stainless steel immersed in antifreeze with the lowest loading values of 169 MPa, showing an infinite ultrasonic fatigue life; while tests subjected to 263 MPa loading stress attains 3.62×106 cycles of ultrasonic fatigue life. The scanning electron microscopy visualizations for both cases of immersion tests showed that the initiation and propagation of the crack occurred on the surface of the specimens, exhibiting the typical mechanical fracture behavior without any apparent thermal influence.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright (c) 2024 Luis M. Torres Duarte, Gonzalo Mariano Domínguez Almaraz, Hipólito M. Venegas Montaño
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.