An investigation of cracks caused by concrete shrinkage and temperature difference in common reinforced concrete bridge structures.
DOI:
https://doi.org/10.3221/IGF-ESIS.68.16Keywords:
Crack in reinforced concrete, Concrete bridges, Tension chord model, Crack width, Concrete shrinkage and temperature differences, Crack controlAbstract
This research investigates cracking in Reinforced Concrete Structures (RCS), particularly in bridge abutments, box girders, and culverts. Cracks often appear even after the concrete has reached its full strength. The current American Bridge Design Standard (AASHTO) permits cracks but doesn’t specify quantitative limits on crack widths. This study uses the fib MODEL CODE 2010 (fib) to analyze RCS under shrinkage and temperature loading. It was found that cracks often exceed fib’s allowable limits, primarily due to significant temperature differences between concrete and steel reinforcement. This is especially prevalent in larger structures with high hydration heat. The use of smaller diameter reinforcement can significantly reduce crack width compared to larger ones, given the same steel ratio. However, a high steel ratio, while reducing crack width, increases susceptibility to cracking. Cracks typically occur after several weeks to months, with widths ranging from 0.30 to 0.70 millimeters due to shrinkage and temperature differences. These findings underscore the importance of considering both shrinkage and temperature differences in the design and maintenance of RCS. By understanding the impact of these factors, as well as the role of reinforcement diameter and steel ratio, engineers can develop more effective strategies for managing and mitigating cracking.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright (c) 2024 Van-Hau Nguyen
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.