Effect of Ti addition and cast part size on solidification structure and mechanical properties of medium carbon, low alloy cast steel
DOI:
https://doi.org/10.3221/IGF-ESIS.62.15Keywords:
Cast steel, Solidification structure, Mechanical propertiesAbstract
In this work, the effect of Ti addition and the cast part size on the solidification structure and mechanical properties of a medium carbon, low alloy cast steel was analyzed. The experimental analysis involved the design of the melts by using Thermo-Calc® software, where different amounts of Ti added to a standard chemical composition of an AISI 13XX steel were simulated. Then, the solidification macrostructure (dendritic pattern and grain size) and microstructure were characterized by using conventional and specific metallographic techniques. Finally, the mechanical behavior in terms of hardness and tensile properties were evaluated.
The results show that the addition of 0.12% of Ti promotes a fine dispersion of Ti nitrides and carbides, but when the Ti concentration raises to 0.2%, the size of the Ti nitrides and carbides increases while its amount decreases. Ti nitrides and carbides particles act as nucleation sites for the precipitation of ferrite from austenite, and it was found that the addition of Ti in the higher concentrations refines the solidification macrostructure (dendritic pattern) for both cast part sizes evaluated.
Regarding mechanical properties, the addition of Ti does not significantly vary the ultimate tensile strength but reduces the total elongation for cast part sizes
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright (c) 2022 Nicolás Emanuel Tenaglia, Diego Fernandino, Alejandro Daniel Basso
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.
How to Cite