Elastoplastic and fracture behaviour of semi-crystalline polymers under multiaxial stress states
DOI:
https://doi.org/10.3221/IGF-ESIS.47.08Keywords:
Semi-crystalline polymers, Fracture, SEM, Stress triaxiality, Multiaxial loading, Butterfly specimenAbstract
The deformation behaviour and fracture mechanisms of high-density polyethylene (HDPE), polypropylene (PP) and polyamide 6 (PA 6) are investigated experimentally under different stress states and at different crosshead speeds of 1, 20 and 200 mm/min. Fracture surface morphologies were investigated in a series of specimens tested at 200 mm/min under combined tension/shear loading at three different loading angles (α = 0°, 30° and 90°) at room temperature (RT) and 50 °C. In addition, the effects of notch profile radii (stress triaxiality) on HDPE, PP and PA 6 fracture behaviour have been studied at RT, using flat and cylindrical notched specimens. Specimens’ geometries were carefully designed to achieve various loading conditions and allowing to explore initial stress triaxialities ranged from 0 in pure shear loading (α = 0°) to a maximum of 0.84 for flat notched specimens with radius of 5 mm. The yield load shows an explicit dependency on temperature and crosshead speed. The fracture surfaces analysed reveals damage mechanisms such as crazing, void and cavitation formation. Two or more mechanisms are predominant, which means that the stresses along fracture process are not uniform.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.