Crack initiation behavior of notched specimens on heat resistant steel under service type loading at high temperature
DOI:
https://doi.org/10.3221/IGF-ESIS.38.04Keywords:
10%Cr steel, Notched, Lifetime, Neuber, von MisesAbstract
Cracks at notches deserve special consideration in the design of steam turbine components. This work is addressed to investigate the crack initiation behavior a 10%Cr rotor steel with the help of notched specimens
under service-type loading. A significant drifting down of the peak-values of axial deformation under constant amplitude load was observed. Crack initiation was evaluated with the help of the relationship between irreversible deformation energy and cycle number. Further, metallographic examinations were employed to characterize the superposition of creep and fatigue damage mechanisms. Both Neuber-hypothesis and von Mises equivalent strain at notch root were applied for lifetime prediction. Finally, the effectiveness of
both methods is validated by comparing with experimental results.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.
How to Cite