Durability method on corrosion fatigue performance of AH 32 steel
DOI:
https://doi.org/10.3221/IGF-ESIS.48.46Keywords:
Durability method, Corrosion fatigue, Thermal spraying, Crack nucleation, Crack propagationAbstract
A durability method in view of cathodic protection is proposed to improve the corrosion fatigue resistance of AH 32 steel in seawater. By aid of corrosion fatigue tests, the effects of thermal spraying Zn (zinc) and Cr (chromium) coating corrosion fatigue lives are quantitatively determined, respectively, and electrochemical measurement and fracture analysis are used to analyze the life-prolonging mechanism of these two coatings on corrosion fatigue. The results show that both Zn and Cr coating improve the corrosion fatigue resistance of AH 32 steel, and the effect enhances with the decrease of stress. The effect of Cr coating on corrosion fatigue of AH 32 steel mainly reflects in extending the crack initiation life for its better corrosion resistance. While the effect of Zn coating on corrosion fatigue lies in not only inhibiting the initiation of corrosion fatigue but also restraining crack propagation as cathodic protection materials. To sun up, Cr coating has a better durability effect than Zn coating at higher stress level, while Zn exceeds Cr at low stress level.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.
How to Cite