Failure Analysis of Boron Steel Components for Automotive Applications
DOI:
https://doi.org/10.3221/IGF-ESIS.64.09Keywords:
Boron steel, Fine blanking, Spheroidize annealing, Nitrogen pick-up, Hardenability problemsAbstract
The automotive industry is continuously looking for an innovative mix of new steels and manufacturing techniques in order to improve process chain efficiency and cost reduction. To this aim, boron steels are becoming increasingly popular thanks to their high hardenability and machinability. Due to their reduced finishing steps, boron steels are commonly processed using fine blanking technologies.
The success of fine blanking on boron steel components is due to heat treatments which must be carefully designed to avoid precipitation of boron-rich compounds that would lower steel hardenability. At high temperature, boron is very reactive with oxygen and nitrogen.
The main focus of this paper is to show some drawbacks that can occur during heat treatments of automotive components. An experimental campaign was performed on two different boron steels, namely EN 34MnB5 and EN 22MnB5. The steel samples were previously spheroidized annealed in a neutral environment (hydrogen/nitrogen atmosphere), and then fine blanked to obtain specific automotive components which were subsequently quenched and tempered. Experimental tests revealed precipitation of nanometric compounds, causing strong grain refinement and localized decrease of steel hardenability. Hardenability problems were brought back to nitrogen pick-up during initial spheroidize annealing treatments.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright (c) 2023 Marco Virginio Boniardi, Andrea Casaroli, Laura Sirangelo, Sergio Monella, Michele Mazzola
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.
How to Cite