Influence of themo-mechanical treatments and microstructural state on the fatigue behaviour of a weald seam: case of API X60 steel
DOI:
https://doi.org/10.3221/IGF-ESIS.58.26Keywords:
Fatigue crack, Thermal-mechanical treatment, microstructure of welded joints, crack propagation, mechanical properties of API X60 steel, chemical composition.Abstract
The aim of this work is the study of the fatigue behaviour of API X60 steel and the influence of thermal and mechanical treatments. The evaluation of the integrity and safety of welded structures dictates the approach taken in this research. The microstructural observations on the different zones of the weld seam indicates that the variation of heterogeneous structure is a progressive destruction of the strips of lamination which cause a new phase leading to a drop in the mechanical properties requiring treatment after welding. The fatigue cracking rate diverges beyond the threshold of DK, but no deviation of the crack from its propagation axis was noticed, which confirms the correct choice of filler metal over that of the base metal with an overmatching M = 1.1, and the treatments applied to the structure. This fatigue cracking rate transversal to the welding direction initially presents an aspect similar to that of BM but registers a delay as soon as the crack tip enters the second zone (HAZ) then it progresses rapidly. This evolution is characterized by a disturbance due to the repeated change of microstructure.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright (c) 2021 Mohammed Achoui , Fethi Sebaa, Benattou Bouchouicha
This work is licensed under a Creative Commons Attribution 4.0 International License.
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.
How to Cite