Influence of microstructure on fatigue property of ultra high-strength steels
DOI:
https://doi.org/10.3221/IGF-ESIS.48.15Keywords:
Ultra-high-strength steel, Fatigue, 4-point bending, Fatigue crackAbstract
Ultra-high-strength steels (with tensile strength higher than 980 MPa) are widely used in automobile manufacturing owing to their lightweight that contributes to fuel efficiency. The fatigue strength of ultra-high-strength steels with a notch tends to decrease, which is known as the effect of notch sensitivity. In this study, 4-point bending fatigue tests were performed to examine the fatigue strength and notch sensitivity of four steels; namely 590 MPa class steel, 980 MPa class martensitic steel, 980 MPa class bainitic steel, and 980 MPa class precipitation hardening steel plates with three different stress concentration factors. The results indicate that the fatigue strength and notch sensitivity of 980 MPa class steel specimens were higher than those of 590 MPa class steel specimens. The notch sensitivities of tested plate specimens were lower than those reported for cylindrical specimens of bainitic ultra-high-strength steels. Fatigue crack observation revealed that the cracks initiated in 590 MPa class steel, 980 MPa class bainitic, and martensitic steel propagated southward from the lowest bottom of notch. Although similar initial crack propagation pattern was detected in precipitation hardening steel, the crack changed direction when it reached the central part of the specimen.
Downloads
Downloads
Published
Issue
Section
Categories
License
Copyright
Authors are allowed to retain both the copyright and the publishing rights of their articles without restrictions.
Open Access Statement
Frattura ed Integrità Strutturale (Fracture and Structural Integrity, F&SI) is an open-access journal which means that all content is freely available without charge to the user or his/her institution. Users are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles in this journal without asking prior permission from the publisher or the author. This is in accordance with the DOAI definition of open access.
F&SI operates under the Creative Commons Licence Attribution 4.0 International (CC-BY 4.0). This allows to copy and redistribute the material in any medium or format, to remix, transform and build upon the material for any purpose, even commercially, but giving appropriate credit and providing a link to the license and indicating if changes were made.